CHARCTERISTICS
OF CERAMICS
Material1
/ Material2 / Material3
/ Material4
MATERIAL |
ALUMINA(Al2O3) |
ZIRCONIA(ZrO2)
|
99.5% |
99.9% |
Y Type |
Mg Type |
Color |
White |
Ivory |
Ivory |
Yellow |
Density |
3.8 |
3.9 |
6.0 |
5.7 |
Vickers Hardness Load(500g) |
Kgf/mm2 |
1700 |
1750 |
1250 |
1100 |
GPa |
16.7 |
17.2 |
12.3 |
10.8 |
Flexural Strength |
Kgf/mm2 |
33 |
50 |
100 |
70 |
Gpa |
323 |
490 |
980 |
686 |
Compressive Strength |
Kgf/mm2 |
240 |
- |
580 |
- |
Mpa |
2353 |
- |
5686 |
- |
Young's Modulus of Elasticity |
X106Kgf/Cm2 |
3.7 |
3.9 |
2.1 |
2.1 |
GPa |
362 |
382 |
206 |
206 |
Coefficient of Linear Thermal
Expansion (x10-6/¡É) |
40 ~ 400¡É |
7.1 |
7.2 |
10.5 |
9.9 |
40 ~ 800¡É |
7.9 |
8.0 |
11.0 |
10.3 |
Thermal Conductivity(20¡É) (cal*cm/cm2*sec*¡É)
|
0.06 |
0.08 |
0.009 |
0.008 |
Fracture Toughness (MN/m3/2)
|
3.4 |
3.4 |
6.0 |
11.5 |
Max. Use Temperature (¡É)
|
1600 |
1750 |
200 |
800 |
Thermal Shock Resistance
|
¡É |
250 |
250 |
300 |
450 |
¢µ |
482 |
482 |
572 |
842 |